本文利用经典多体分子动力学模拟研究了包含10到100个原子的$Fe_n$纳米团簇的熔化相变行为。对于许多团簇尺寸而言，表面熔化发生在比核心熔化低得多的温度下。计算了所有团簇尺寸下的表面熔点、核心熔点以及能量熔点（最大热容$C_v$对应的温度）。结果表明熔化特性强烈依赖于团簇结构。具有闭壳层结构的团簇总是表现出一阶类相变特征。由于存在多个能量相近的结构构型，分析范围内的几乎三分之一的团簇尺寸表现出二阶类相变特征。相较于闭壳层结构，多出一个或几个原子的一壳层团簇具有非常低的表面熔点和非常高的能量熔点。在某些核结构的50个原子以上的团簇中，观察到了表面先于核心发生熔化的现象。

In this work, the melting phase transitions of $Fe_{n}$ nanoclusters with $10 \leq n \leq 100$ atoms are investigated using classical many-body molecular dynamics simulations. For many cluster sizes, surface melting occurs at much lower temperatures than core melting. Surface and core melting points, and energetic melting points (temperatures of maximum heat capacity, $C_v$) are calculated for all cluster sizes. Melting properties are found to be strong functions of cluster structure. Cluster sizes with closed-shell structures always have first-order-like phase transitions. Almost one-third of cluster sizes in the analyzed range exhibit second-order-like phase transitions due to the presence of multiple structural configurations close in energy. 1-shell clusters with one to a few more atoms than a neighboring closed-shell structure have very low surface melting points and very high energetic melting points compared to their closed-shell counterparts. In clusters above 50 atoms with certain core structures, melting of the surface before the core was observed.