反铁磁体（AM）是一类奇异的反铁磁材料，即使在净全局磁化为零且自旋轨道耦合（SOC）效应缺失的情况下，也会表现出自旋分裂现象。本文理论研究了各向异性超导体/反铁磁体/各向异性超导体（ISC/AM/ISC）约瑟夫森结中的超电流非互易性，揭示了不对称的约瑟夫森临界电流、0-π转变以及异常的电流-相位关系（CPR）。即使在没有自旋轨道耦合的情况下，由于反铁磁体强度和取向的综合作用，传统超导体中观察到了显著的约瑟夫森二极管效率（JDE）。然而，在内禀自旋轨道耦合（ISOC）存在时，这种效应显著增强，导致单带和双带ISC/AM约瑟夫森结中均出现了明显的二极管效应。此外，研究发现，无论在哪种情况下，JDE在较高反铁磁体强度和中间取向时更为显著，而在0°和45°取向时明显减弱。我们的结果还表明，势垒透明度和反铁磁体长度对优化JDE起着至关重要的作用。在单带ISC/AM系统中，JDE对于任何反铁磁体长度都持续存在，而在双带ISC/AM系统中，较长的反铁磁体结会导致JDE减弱。此外，我们的研究结果表明，在考虑强反铁磁体强度的情况下，无论是单带还是双带ISC/AM约瑟夫森结，都可以实现约52%的二极管效率。值得注意的是，单带ISC提供了更宽的反铁磁体取向范围，这有助于更好地调节和优化JDE。我们的研究结果揭示了反铁磁体强度、取向和内禀自旋轨道耦合对JDE效率的影响，为超导二极管的设计提供了重要见解。

Altermagnets (AMs) are an exotic class of antiferromagnet that exhibit spin-splitting even at the absence of net global magnetization and spin-orbit coupling (SOC) effects. In this work, we investigated theoretically, the supercurrent nonreciprocity in an Ising Superconductor/Altermagnet/Ising Superconductor (ISC/AM/ISC) Josephson junction which revealed asymmetric Josephson critical currents, $0 - \pi$ transitions and anomalous current-phase relationship (CPR). A strong Josephson diode efficiency (JDE) is observed due to the combined effects of AM strength and orientations in a conventional SC even in absence of SOC. However, it significantly enhances in presence of intrinsic SOC (ISOC), resulting in pronounced diode effect in both single and double band ISC/AM based Josephson junction. Additionally, it is observed that JDE is more prominent at higher AM strengths with intermediate orientations in all scenario. Notably, it is significantly suppressed for orientations $0^\circ$ and $45^\circ$. Our results also indicate that barrier transparency and AM lengths play a crucial role in optimizing the JDE. In a single-band ISC/AM system JDE persists for any AM length, while reduces at longer AM junction in case of a double-band ISC/AM system. Moreover, our results suggest that a diode efficiency of $\sim 52\%$ can be achieved in the proposed Josephson junction in both single and double band ISC/AM Josephson junction by considering strong AM strength. Furthermore, single band ISC offers wide AM orientation range in contrast to double band ISC for better tunability and optimization of JDE. Our findings highlight the impact of AM strength, orientation and ISOC on the JDE efficiency offering insights for superconducting diode design.