具有非中心对称（NC）结构的中熵合金（MEA）或高熵合金（HEA）以及Re基化合物为探索非常规超导性提供了肥沃的研究土壤。本文成功合成了五种之前未报道的具有α-Mn晶格的NC Re基MEA-HEA超导体，其超导转变温度（Tcs）范围在4到5 K之间。通过成分调整调控价电子数（VEC），可以提高超导转变温度（Tc）。磁化测量结果表明，所有合成的Re基MEA-HEA均为体心II型超导体。比热分析显示这些HEA的超导态可以用单一s波模型很好地描述。研究发现，这些α-Mn MEA/HEA超导体的Kadowaki-Woods比率接近重费米子化合物的典型值，表明存在强电子关联。这些发现为研究非中心对称MEA-HEA中超导性起源中的高无序性提供了有前景的材料平台。

Medium or high-entropy alloys (MEAs-HEAs) and rhenium-based compounds with a non-centrosymmetric (NC) structure have received a lot of attention for offering a fertile soil in search for unconventional superconductivity. Here, five previously unreported NC Re-based MEA-HEA superconductors with an $\alpha$-Mn lattice are successfully synthesized, with their superconducting transition temperatures (Tcs) ranging from 4 to 5 K. An increase in the superconducting transition temperature (Tc) can be achieved by modulating the valence electron count (VEC) through compositional adjustments. Magnetization measurements confirm that all the synthesized Re-based MEA-HEAs are bulk type-II superconductors. Specific heat analysis reveals that the superconducting state of these HEAs can be well described by a single-gap s-wave model. Our results show that the Kadowaki-Woods ratio of these $\alpha$-Mn MEA/HEA superconductors are close to the typical value of heavy fermion compounds, suggesting the existence of strong electronic correlation. These findings provide promising material platforms to study the role of high disorder in the origin of superconductivity in the NC MEAs-HEAs.